Blanking is a shearing process where a punch and die are used to create a blank from sheet metal or a plate. The blank is workpiece ejected from the starting stock. The process and machinery are usually the same as that used in piercing, except that the piece being punched out in the piercing process is scrap
Fine blanking
Fine blanking is a specialized form of blanking where there is no fracture zone when shearing. This is achieved by compressing the whole part and then an upper and lower punch extract the blank. This allows the process to hold very tight tolerances, and perhaps eliminate secondary operations.
Materials that can be fine blanked include aluminium, brass, copper, and carbon, alloy and stainless steels.
Fine blanking presses are similar to other metal stamping presses, but they have a few critical additional parts. A typical compound fine blanking press includes a hardened die punch (male), the hardened blanking die (female), and a guide plate of similar shape/size to the blanking die. The guide plate is the first applied to the material, impinging the material with a sharp protrusion or stinger around the perimeter of the die opening. Next a counter pressure is applied opposite the punch, and finally the die punch forces the material through the die opening. Since the guide plate holds the material so tightly, and since the counter pressure is applied, the material is cut in a manner more like extrusion than typical punching. Mechanical properties of the cut benefit similarly with a hardened layer at the cut edge from the cold working of the part. Because the material is so tightly held and controlled in this setup, part flatness remains very true, distortion is nearly eliminated, and edge burr is minimal. Clearances between the die and punch are generally around 1% of the cut material thickness, which typically varies between 0.5–13 mm (0.020–0.51 in). Currently parts as thick as 19 mm (0.75 in) can be cut using fine blanking. Tolerances between ±0.0003–0.002 in (0.0076–0.051 mm) are possible based on material thickness & tensile strength, and part layout.
With standard compound fine blanking processes, multiple parts can often be completed in a single operation. Parts can be pierced, partially pierced, offset (up to 75°), embossed, or coined, often in a single operation. Some combinations may require progressive fine blanking operations, in which multiple operations are performed at the same pressing station.
Fine blanking
Fine blanking is a specialized form of blanking where there is no fracture zone when shearing. This is achieved by compressing the whole part and then an upper and lower punch extract the blank. This allows the process to hold very tight tolerances, and perhaps eliminate secondary operations.
Materials that can be fine blanked include aluminium, brass, copper, and carbon, alloy and stainless steels.
Fine blanking presses are similar to other metal stamping presses, but they have a few critical additional parts. A typical compound fine blanking press includes a hardened die punch (male), the hardened blanking die (female), and a guide plate of similar shape/size to the blanking die. The guide plate is the first applied to the material, impinging the material with a sharp protrusion or stinger around the perimeter of the die opening. Next a counter pressure is applied opposite the punch, and finally the die punch forces the material through the die opening. Since the guide plate holds the material so tightly, and since the counter pressure is applied, the material is cut in a manner more like extrusion than typical punching. Mechanical properties of the cut benefit similarly with a hardened layer at the cut edge from the cold working of the part. Because the material is so tightly held and controlled in this setup, part flatness remains very true, distortion is nearly eliminated, and edge burr is minimal. Clearances between the die and punch are generally around 1% of the cut material thickness, which typically varies between 0.5–13 mm (0.020–0.51 in). Currently parts as thick as 19 mm (0.75 in) can be cut using fine blanking. Tolerances between ±0.0003–0.002 in (0.0076–0.051 mm) are possible based on material thickness & tensile strength, and part layout.
With standard compound fine blanking processes, multiple parts can often be completed in a single operation. Parts can be pierced, partially pierced, offset (up to 75°), embossed, or coined, often in a single operation. Some combinations may require progressive fine blanking operations, in which multiple operations are performed at the same pressing station.
Wow what a great blog, i really enjoyed reading this, good luck in your work. Deep Draw
ReplyDeleteNice post. I learn something more challenging on different blogs everyday. It will always be stimulating to read content from other writers and practice a little something from their store. I’d prefer to use some with the content on my blog whether you don’t mind. Natually I’ll give you a link on your web blog. Thanks for sharing. cnc milling